The rubber extruder completes all the above processes through a barrel with a screw and spiral channel. The plastic pellets enter the barrel through the hopper at one end of the barrel and then are conveyed to the other end of the barrel through the screw. If you want to learn about rubber extruder, you can learn about it through the following.
Here is the content list:
What are the advantages of cold feed extrusion?
What is the purpose and method of cooling the extrudate? :
What is the flow and extrusion expansion of the rubber in the mouth?
Rubber extruder saves heat smelting equipment and is easy to realize mechanization and automation. Moreover, because the main machine strengthens the shearing and plasticization of the screw, the rubber compound can obtain uniform temperature and plasticity; it improves the quality of the extruded products of rubber extruder and improves To improve the surface finish, the extruded semi-finished products have relatively stable and consistent size specifications; the pressure sensitivity of cold feed is small; the application range is wide and the flexibility is large; the investment and production costs of cold feed rubber extruder are low.
The purpose of cooling: to prevent the semi-finished product produced by rubber extruder from self-sulfurization during storage; to restore the rubber to a certain stiffness and prevent deformation; to cool the semi-finished product to shrink and shape.
Cooling method: spray and water tank cooling. To prevent the rubber extruder output from sudden cooling (various degrees of cooling lead to irregular deformation; frosting), it is often cooled with warm water around 40°C, and then further reduced to 20~30°C.
1. The flow of the rubber in the mouth: After the rubber enters the mouth through the runner of the rubber extruder, it is extruded out of the mouth after being subjected to stronger shear and plasticization when passing through the mouth. Therefore, the flow state in the mouth and the size of the mouth structure determine the final shape and quality of rubber extruder products. The rubber material flows through the mouth under the action of the hydrostatic pressure formed by the head of the rubber extruder. Therefore, the rubber material flows through the mouth of the rubber extruder only as an axial movement. Since the thickness of the mouth is generally very thin, the pressure gradient formed by the rubber compound in the mouth is very large.
2. Compression expansion: The rubber is a viscoelastic body. When it flows through the mouth, it undergoes viscous flow and elastic deformation at the same time. When the rubber material enters the mouth from the nose of the rubber extruder, the flow channel is generally narrowed, the flow velocity increases, and a velocity gradient is formed in the flow direction. This speed causes the rubber to produce stretch and elastic deformation. When the orifice flow channel of the rubber extruder is short, the stretch deformation of the rubber is too late to recover, and it will expand after being extruded. (That is, the diameter of the extrudate is larger than the diameter of the mouth shape, and the axial shrinkage occurs). The extruded expansion of rubber extruder mainly depends on the amount of recoverable deformation and the length of relaxation time when the rubber material flows.
Qingdao Huicai Machine Manufacture Co., Ltd developed a rubber extruder. Under the guarantee of quality and price, I think our company's products are worth choosing, so if you need them, please contact us.